SABIC 9X11428J

TYPICAL PROPERTIES¹

TYPICAL VALUE

UNIT

STANDARD

MECHANICAL

Tensile Stress,yld, Type I, 50 mm/min

74

MPa

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

58

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

8

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

15

%

ASTM D638

Tensile Modulus, 5 mm/min

2380

MPa

ASTM D638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

2430

MPa

ASTM D790

Tensile Stress, yield, 5 mm/min

71

MPa

ISO 527

Tensile Stress, break, 5 mm/min

57

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

7

%

ISO 527

Tensile Strain, break, 5 mm/min

22

%

ISO 527

Tensile Modulus, 1 mm/min

2330

MPa

ISO 527

Flexural Stress

91

MPa

ISO 178

Flexural Modulus, 2 mm/min

2270

MPa

ISO 178

IMPACT

lzod Impact, unnotched, 23°C

187

J/m

ASTM D256

Multiaxial Impact

44

J

ISO 6603

Instrumented Dart Impact Total Energy, 23°C

42

J

ASTM D3763

Izod Impact, notched 80*10*4 +23°C

10

kJ/m²

ISO 180/1A

THERMAL

HDT, 0.45 MPa, 3.2 mm, unannealed

213

°C

ASTM D648

HDT, 1.82 MPa, 3.2mm, unannealed

199

°C

ASTM D648

CTE, -30°C to 30°C, flow

5.5E-05

1/°C

ASTM D696

CTE, -30°C to 30°C, xflow

5.5E-05

 1/°C

ASTM D696

HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm

210

°C

ISO 75/Bf

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

196

°C

ISO 75/Af

PHYSICAL

Specific Gravity

1.34

-

ASTM D792

Density

1.34

g/cm³

ASTM D792

Moisture Absorption, (23°C/50% RH/24 hrs)

0.29

%

ASTM D570

Mold Shrinkage, flow, 24 hrs

0.9–2

%

ASTM D955

Mold Shrinkage, xflow, 24 hrs

1–3

%

ASTM D955

Moisture Absorption (23°C / 50% RH)

0.4

%

ISO 62

INJECTION MOLDING

Drying Temperature

120

°C

Drying Time

4

Hrs

Maximum Moisture Content

0.05

%

Melt Temperature

240–265

°C

Front - Zone 3 Temperature

260–270

°C

Middle - Zone 2 Temperature

245–255

°C

Rear - Zone 1 Temperature

220–230

°C

Mold Temperature

80–100

°C

Back Pressure

0.2–0.3

MPa

Screw Speed

30–60

rpm