奇美PH-888H 奇美高抗冲聚苯乙烯HIPS原料

特性
(Properties)

测试方法(Test Method)

测试條件(Test Condition)

单位(Unit)

PH-888H

引张强度
Tensile Strength

ASTM D638

18*,6 mm/min

Kg/cm²(lb/in²)

300(4260)

延伸率
Tensile Elongation

ASTM D638

18*,6 mm/min

%

70

弯曲强度
Flexural Strength

ASTM D790

14",2.8 mm/min

Kg/cm²(lb/in²)

440(6250)

 弯曲弹性率
Flexural Modulus

ASTM D790

14",2.8 mm/min

Kg/cm2(lb/in2)

20000(280000)

 IZOD冲击强度
Izod Impact Strength

ASTM D256(Notched)

14",23℃
18*,23℃

Kg-cm/cmf(f-lb/in)
Kg-cm/cmf(f-lb/in)

8.0(1.38)
11.0(2.02)

流动系数
Melt Flow Index

ASTM D1238

200℃,5Kg

g/l0min

3.6

硬度
Hardness

ASTM D785

1/4"

L Scale

85

比重
Specific Gravity

ASTM D792

23℃

-

1.05

软化点
Vicat Softening Temp

ASTM D1525

18", 50℃/hr

℃(℉)

80(176)

热变形温度
H.D.T Annealed(85 ℃,8hr)Unannealed

ASTM D648

14", 120℃/hr

℃(℉)

1/16"HB

燃烧率
Flammability

UL 94

-

-

1/16"HB